MarinaQuadro BWP

A marine-grade plywood complying with E0 emission norms, emitting negligible amounts of formaldehyde, making your interiors a safe space. Our VierPro technology with 4 steps of Hot and Cold pressing lends uniformity and is compressed to give extra strength. Being Marine BWP grade ply it is naturally immune to termite attacks, borer, and fungus . Backed by a solid 30-year warranty, MarinaQuadro is the most preferred plywood, and can be used for making best-in-class and long-enduring furniture, modular kitchen cabinets.

Thickness (MM)

    6 MM, 8 MM, 12MM, 15 MM, 18MM, 25 MM

Sizes (MM)

    2440 MM X 1220 MM
    2135 MM X 1220 MM
    1830 MM X 1220 MM

Application

Borer & Termite Proof

Boiling Waterproof

Matt Ply

IS 710

Fully Calibrated

VierPro Technology

30 Years Warranty

E-0 Emission Level

PF - Glue Line Protection

Premium Gurjan Face

SR NO. Tests Method ISI Requirements Observed Values
1 Dimension Squareness Length :+ 6mm
Width :+ 3mm
Thicknes :+/- 5%
Max : 0.20%
Length- 2442 mm
Width- 1221 mm
Thickness- 19 mm
Squareness - 0.16%
2 Moisture content Moisture content should not be less than 5% and not more than 15% 7.65%
3 Glue Adhesion in Dry State
(a) Glue Shear Strength

Avg.: 1350 N
Min. Individual: Avg.: 1100 N

1411 N
1176 N
(b) Adhesion of Plies Bond shall show minimum Pass
Standard, Poor or Excellent
Satisfactory
4 Water Resistance Test
(After 72 Hours boiling in water)

(a) Glue Shear Strength

Average : 1000 N
Minimum Individual : 800 N

1249 N
915 N
(b) Adhesion of Plies Bond shall show minimum Pass
Standard, Poor or Excellent
Satisfactory
5 Tensile Strength
(a) Along the grain direction

Should not be less than 42.0 N/mm²

54.20 N/mm²
(b)Across the grain direction Should not be less than 25.0 N/mm² 41.82 N/mm²
(c) Sum of both the direction Should not bf less than 84.5 N/mm² 96.02 N/mm²
6 Mycological Test
(a) Glue Shear Strength

Average 1000 N
Minimum lndividual : 800 N

1250 N
1010 N
(b) Adhesion of Plies Adherent fibre distributed more or less uniformly Excellent
7 STATIC BENDING STRENGTH ( DRY STATE )
Modulus of Elasticity
(a) Along the grains of the face Veneer

Average: 7500 N/mm²
Min. lndividual-6700 N/mm²

7950 N/mm²
7270 N/mm²
b) Across the grain of the Face Veneer Average: 4000 N/mm²
Min. lndividual-3600 N/mm²
4845 N/mm²
4115 N/mm²
Modulus of Rupture
(a) Along the grains of the face Veneer

Average: 50 N/mm²
Min. lndividual-45 N/mm²

60 N/mm²
55 N/mm²
(b) Across the grain of the Face Veneer Average: 30 N/mm²
Min. lndividual-27 N/mm²
36 N/mm²
29 N/mm²
8 STATIC BENDING STRENGTH ( WET STATE )
Modulus of Elasticity
(a) Along the grains of the face Veneer

Average: 3570 N/mm²
Min. lndividual- 3400 N/mm²

4525 N/mm²
3770 N/mm²
b) Across the grains of the Face Veener Average: 2000 N/mm²
Min. lndividual-1800 N/mm²
2845 N/mm²
2215 N/mm²
Modulus of Rupture
(a) Along the grains of the face Veneer

Average: 25 N/mm²
Min. lndividual-22 N/mm²

30 N/mm²
25 N/mm²
(b) Across the grains of the Face Veener Average: 15 N/mm²
Min. lndividual-13
21 N/mm²
15 N/mm²

Download the brochure for more information