MarinaQuadro
A marine-grade plywood complying with E0 emission norms, emitting negligible amounts of formaldehyde, making your interiors a safe space. Our VierPro technology with 4 steps of Hot and Cold pressing lends uniformity and is compressed to give extra strength. Being Marine BWP grade ply it is naturally immune to termite attacks, borer, and fungus.Backed by a solid 25-year warranty, MarinaQuadro is the most preferred plywood, and can be used for making best-in-class and long-enduring interior and exterior furniture, modular kitchen cabinets, and even ship building.
Sizes (Available in mm):
Application
-
Structural Home Building
-
Kitchen
-
Garden Furniture
-
Outdoor Flooring
Borer & Termite Resistance
Boiling Waterproof
Matt Finish
E-0 Emission Level
IS 710
100% Calibrated
VierPro Technology
25 Years Warranty
| SL NO. | Tests Method | ISI requirements | Observed Values |
|---|---|---|---|
| 1 | Dimension Squareness | Length :+ 6mm Width :+ 3mm Thicknes :19mm ± 5% Max : 2mm/1000mm |
Length- 2442 Width- 1221 Thickness- 18.7mm Squareness - 0.96 |
| 2 | Moisture content | Moisture content should not be less than 5% and not more than 15% | 7.65% |
| 3 | Glue Adhesion in Dry State (a) Glue Shear Strength |
Avg.: 1350 N Minm Individual: Avg.: 1000 N |
1411 N 1176 N |
| (b) Adhesion of Plies | Bond shall show minimum Pass Standard, Poor or Excellent |
Satisfactory | |
| 4 | Water Resistance Test (a) Glue Shear Strength |
Average : 1350 N Minimum Individual : 1100 N |
1249 N 915 N |
| (b) Adhesion of Plies | Bond shall show minimum Pass Standard, Poor or Excellent |
Satisfactory | |
| 5 | Tensile Strength (a) Along the grain direction |
Should not be less than 42.0 N/mm2 | 61.93 N/mm2 |
| (b) Across the grain direction | Should not be less than 25.0 N/mm2 | 39.52 N/mm2 | |
| (c) Sum of both the direction | Should not bf less than 84.5 N/mm2 | 101.45 N/mm2 | |
| 6 | Mycological Test (a) Glue Shear Strength |
Average 1000 N Minimum lndividual : 800 N |
1250 N 1010 N |
| (b) Adhesion of Plies | Adherent fibre distributed more or less uniformly | Exellent | |
| 7 | STATIC BENDING STRENGTH (DRY STATE) | ||
| Modulus of Elasticity (a) Along the grains of the face Veneer |
Average: 7500 N/mm2 Min. lndividual-6700 N/mm2 |
8515 N/mm2 7270 N/mm2 |
|
| b) Across the grain of the Face Veneer | Average: 4000 N/mm2 Min. lndividual-3600 N/mm2 |
4845 N/mm2 4115 N/mm2 |
|
| Moduls of Rapture (a) Along the grains of the face Veneer |
Average: 50 N/mm2 Min. lndividual-45 N/mm2 |
68 N/mm2 55 N/mm2 |
|
| (b) Across the grain of the Face Veneer | Average: 30 N/mm2 Min. lndividual-27 N/mm2 |
48 N/mm2 29 N/mm2 |
|
| 8 | STATIC BENDING STRENGTH (WET STATE ) | ||
| Modulus of Elasticity (a) Along the grains of the face Veneer |
Average: 3570 N/mm2 Min. lndividual- 3400 N/mm2 |
8515 N/mm2 3770 N/mm2 |
|
| b) Across the grain of the Face Veneer | Average: 2000 N/mm2 Min. lndividual-1800 N/mm2 |
2845 N/mm2 2215 N/mm2 |
|
| Moduls of Rapture (a) Along the grains of the face Veneer |
Average: 25 N/mm2 Min. lndividual-22 N/mm2 |
37 N/mm2 25 N/mm2 |
|
| (b) Across the grain of the Face Veneer | Average: 15 N/mm2 Min. lndividual-13 N/mm2 |
21 N/mm2 15 N/mm2 |
|
Download the brochure for more information